Comparative Analysis of the Mechanical Properties and Biocompatibility between CAD/CAM and Conventional Polymers Applied in Prosthetic Dentistry.

Modern media often portray CAD/CAM technology as widely utilized in the fabrication of dental prosthetics. This study presents a comparative analysis of the mechanical properties and biocompatibility of CAD/CAM (Computer-Aided Design/Computer-Aided Manufacturing) polymers and conventional polymers commonly utilized in prosthetic dentistry. With the increasing adoption of CAD/CAM technology in dental laboratories and practices, understanding the differences in material properties is crucial for informed decision-making in prosthodontic treatment planning. Through a narrative review of the literature and empirical data, this study evaluates the mechanical strength, durability, esthetics, and biocompatibility of CAD/CAM polymers in comparison to traditional polymers. Furthermore, it examines the implications of these findings on the clinical outcomes and long-term success of prosthetic restorations. The results provide valuable insights into the advantages and limitations of CAD/CAM polymers, informing clinicians and researchers about their suitability for various dental prosthetic applications. This study underscores the considerable advantages of CAD/CAM polymers over conventional ones in terms of mechanical properties, biocompatibility, and esthetics for prosthetic dentistry. CAD/CAM technology offers improved mechanical strength and durability, potentially enhancing the long-term performance of dental prosthetics, while the biocompatibility of these polymers makes them suitable for a broad patient demographic, reducing the risk of adverse reactions. The practical implications of these findings for dental technicians and dentists are significant, as understanding these material differences enables tailored treatment planning to meet individual patient needs and preferences. Integration of CAD/CAM technology into dental practices can lead to more predictable outcomes and heightened patient satisfaction with prosthetic restorations.

A 3D-simulation study of the deformation, tension, and stress of 3D-printed and conventional denture base materials after immersion in artificial saliva.

INTRODUCTION: The worldwide application of digital technology has presented dentistry with transformative opportunities. The concept of digital dentures, incorporating computer-aided design (CAD) and computer-aided manufacturing (CAM) techniques, holds the promise of improved precision, customization, and overall patient satisfaction. However, the shift from traditional dentures to their digital counterparts should not be taken lightly, as the intricate interplay between oral physiology, patient comfort, and long-term durability requires thorough examination.

Changes in the Surface Texture of Thermoplastic (Monomer-Free) Dental Materials Due to Some Minor Alterations in the Laboratory Protocol-Preliminary Study.

Contemporary thermoplastic monomer-free prosthetic materials are widely used nowadays, and there are a great variety available on the market. These materials are of interest in terms of the improvement of the quality features of the removable dentures. The aim of this study is to establish how minimal changes in the laboratory protocol of polyamide prosthetic base materials influence the surface texture. Two polyamide materials intended for the fabrication of removable dentures bases were used-Perflex Biosens (BS) and VertexTM ThermoSens (TS). A total number of 20 coin-shaped samples were prepared. They were injected under two different modes-regular, as provided by the manufacturer, and modified, proposed by the authors of this study. Scanning electronic microscopy (SEM) under four magnifications-×1000, ×3000, ×5000, and ×10,000-was conducted. With minimal alterations to the melting temperature (5 °C) and the pressure (0.5 Bar), in Biosens, no changes in terms of surface improvement were found, whereas in ThermoSens, the surface roughness of the material significantly changed in terms of roughness reduction. By modifying the technological mode during injection molding, a smoother surface was achieved in one of the studied materials.

Colour Stability of 3D-Printed and Prefabricated Denture Teeth after Immersion in Different Colouring Agents-An In Vitro Study.

This study investigated the colour stability of three dimensional (3D)-printed and conventional denture teeth after immersion in different colourants. A total of 60 artificial maxillary central incisors were selected from three types of materials: 3D-printed dental resin (NextDent, 3D Systems, Soesterberg, The Netherlands), prefabricated acrylic teeth in Ivostar Shade (Ivoclar Vivadent, Schaan, Liechtenstein), and SpofaDent Plus in shade A2 (SpofaDental, Jicín, Czechia). These were immersed in four types of colourants at room temperature (23 °C ± 1 °C), including artificial saliva (pH = 6.8) as a control group, coffee, red wine, and Coca-Cola (n = 5). The temperature and the pH of the colouring agents were maintained throughout all immersion periods. After 7 days (T1), 14 days (T2), and 21 days (T3), the ∆E values were measured with a SpectroShade Micro (SpectroShade, Oxnard, CA, USA) spectrophotometer. Their means were then calculated and compared by two-way ANOVA. The independent factors, immersion time and different staining solutions, as well as the interaction between these factors, significantly influenced ΔE. The highest and the lowest mean ∆Es were recorded for prefabricated teeth in red wine, and 3D-printed teeth in artificial saliva, respectively. All the specimens demonstrated an increased colour change at T1 compared to T3, and the difference in mean ∆E was statistically significant.

Linear Dimensional Change and Ultimate Tensile Strength of Polyamide Materials for Denture Bases.

The aim of the current study was to evaluate the dimensional changes and ultimate tensile strength in three polyamide materials for denture bases fabrication through injection molding, subjected to artificial aging and different storage conditions. A total of 333 test specimens fabricated from Biosens (BS; Perflex, Netanya, Israel), Bre.flex 2nd edition (BF; Bredent, Senden, Germany) and ThermoSens (TS; Vertex Dental B.V., Soesterberg, The Netherlands)-n = 111 per material-were equally divided into three groups (n = 37) based on different treatments and storage conditions. Test samples allocated to the "Control group" were not artificially aged and stored in water for 24 h. Both "Treatment 1 group" and "Treatment 2 group" were subjected to thermocycling, the former dehydrated and the latter stored in water between cycle-sets. Linear changes and ultimate tensile strength were measured and analyzed for storage condition and material influence on the outcome variables. A Welch ANOVA test with Games-Howell post-hoc analysis was used to compare the influence of treatments across different materials. Significant differences were found for all three included materials with p values ranging from <0.05 to <0.001 for linear dimensional changes. The magnitude of alterations varied and was large for BS (Perflex, Israel) (ω2 = 0.62) and BF (Bredent, Germany) (ω2 = 0.47) and small but significant for TS (Vertex Dental B.V., The Netherlands) (ω2 = 0.05). However, results seem to fall into clinically acceptable range. Significant differences were also observed for the ultimate tensile strength test with the same range of p-values. All three materials showed different initial ultimate tensile strengths and varying reaction to artificial aging and storage with the lowest alterations observed for BF (Bredent, Germany) (ω2 = 0.05). Within the limitation of this study, it can be concluded that all three materials show different dimensional and mechanical properties when subjected to artificial aging and different storage. Although linear dimensions show significant changes, they seem to be clinically irrelevant, whereas the change in ultimate tensile strength after only 6-month equivalent clinical use was substantial for BS (Perflex, Israel) and TS (Vertex Dental B.V., The Netherlands).

Injection Shrinkage аnd Water Sorption of Some Thermoplastic Dental Materials

Objective: To evaluate the change of diameter of different injection-molded thermoplastic materials. Material and Methods: Four thermoplastic injection-molded materials were analyzed (Bre.flex 2nd edition, Vertex ThermoSens, Perflex Biosens and Polyan IC). A total of 432 test samples were made in the form of an "hourglass". All samples were divided into three groups: Group I (Control) - consisting of 36 test samples for each type of material, that was not exposed to artificial aging or a wet environment; Group II - consisting of 36 test samples for each type of material, that were artificially aged through dehydration; Group III - specimen were subjected to artificial aging without dehydration. The diameter of each specimen was measured with a digital caliper. Data were analysed using the Student's t-test. Results: Regarding to shrinkage, the samples from the Bf Control group have a mean value of 1.56 mm and was observed a shrinkage of the injection-molded polyamide material within 0.25%. The comparison between the samples from Group II and Group III showed statistically significant differences (p<0.001). There were no significant differences between groups for Thermosens and Biosens (p>0.05). The comparison between Group II and Group III for Polyan IC samples shows that Group III has a higher arithmetic mean value (p<0.01). Conclusion: Shrinkage of the polymers during the injection process is present in all materials. The thermocycling and the storage in a dry or in a wet environment of the samples results in a change of the diameter in almost every single type of material.